Super Duplex Tube
Duplex Stainless Steel have a structure that contains both ferrite and austenite. Duplex alloys have higher strength and better stress corrosion cracking resistance than most austenitic alloys and greater toughness than ferritic alloys, especially at low temperatures. The corrosion resistance of duplex alloys depends primarily on their composition, especially the amount of chromium, molybdenum, and nitrogen they contain
Standard: ASTM/ASME A/SA789, A/SA790, A/SA928, DIN17456/17458, EN10216-5. After negotiation, we can supply pipe with customer's special requirement. |
Material Grade: Chemical Composition
UNS |
EN |
DIN |
C % |
Cr% |
Ni% |
Mo% |
N% |
Other % |
S31803 |
1.4462 |
X2CrNiMoN22-5-3 |
0.030max |
21.0-23.0 |
4.5-6.5 |
2.5-3.5 |
0.08-0.20 |
/ |
S32205 |
1.4462 |
X2CrNiMoN22-5-3 |
0.030max |
22.0-23.0 |
4.5-6.5 |
3.0-3.5 |
0.14-0.20 |
/ |
S32101 |
1.4162 |
|
0.040max |
21.0-22.0 |
1.35-1.70 |
0.10-0.80 |
0.20-0.25 |
Cu 0.10-0.80 |
S32304 |
|
|
0.030max |
21.5-24.5 |
3.0-5.5 |
0.05-0.60 |
0.15-0.20 |
Cu 0.05-0.60 |
S32750 |
1.4410 |
X2CrNiMoN25-7-4 |
0.030max |
24.0-26.0 |
6.0-8.0 |
3.0-5.0 |
0.24-0.32 |
Cu 0.50max |
S32760 |
|
|
0.050max |
24.0-26.0 |
6.0-8.0 |
3.0-4.0 |
0.20-0.30 |
Cu 0.50-1.00 |
Mechanical Property:
UNS |
Tensile Strength Min, Mpa |
Yield Strength Min, Mpa |
Elongation in 2 in Or 50mm Min, % |
Hardness Max, HRC |
S31803 |
620 |
450 |
25 |
30 |
S32205 |
655 |
485 |
25 |
30 |
S32101 |
700 |
530 |
30 |
30 |
S32304 |
690 |
450 |
25 |
30 |
S32750 |
800 |
550 |
15 |
32 |
S32760 |
750 |
550 |
25 |
32 | |